Oxidative crosslinking of copolyimides at sub-T g temperatures to enhance resistance against CO 2 -induced plasticization

Research output: Contribution to journalArticle

Related Edinburgh Organisations

Original languageEnglish
Pages (from-to)40-48
Number of pages9
JournalJournal of Membrane Science
Volume583
Early online date5 Apr 2019
DOIs
Publication statusPublished - 1 Aug 2019

Abstract

Polymer crosslinking via thermal oxidation is a well-established technique that enhances the gas selectivity of a polymer membrane, but usually at the expense of lower gas permeability. As thermal oxidation is typically performed at temperatures higher than the glass transition temperature (T g )of polymers, large energy footprints are incurred while pore structures in asymmetric membranes – the preferred physical configuration of polymer membranes are collapsed. To overcome these drawbacks, here we report a strategy to simultaneously enhance both gas permeability and selectivity via thermal oxidation at sub-T g temperatures. This was achieved with a copolymer consisting a component that enhanced T g , and another component with functional groups that decomposed and induced crosslinking at lower temperatures. We used a series of complementary characterization techniques to pinpoint the actual mechanism underpinning our sub-T g thermal oxidation approach. Crosslinking slightly reduced the d-space between polymer chains but increased polymer fractional free volume and most importantly, inhibited CO 2 -induced plasticization. The pure CO 2 permeability of the crosslinked polymer reached 88.5 Barrer with a CO 2 /CH 4 ideal selectivity of 38.8, while no plasticization behavior was detected at a CO 2 pressure up to 30 atm at 35 °C. When separating CO 2 :CH 4 (1:1)mixed gas at total pressures between 10 and 60 atm, the CO 2 permeability and CO 2 /CH 4 selectivity of this crosslinked polymer were reduced to 55 Barrer and 29 due to competitive permeation.

    Research areas

  • Crosslinking mechanism, Gas separation membrane, Natural gas purification, Plasticization resistance, Sub-T thermal oxidative crosslinking